| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | | ASTM792 | 1.04 | g/cm3 |
| 熔流率（熔体流动速率）(220°C/10.0kg) | | ASTM1238 | 6.0 | g/10min |
| 收缩率-流动(3.20mm) | | ASTM955 | 0.40to0.70 | % |
| 机械性能 | 抗张强度2(屈服,3.20mm) | | ASTM638 | 44.1 | MPa |
| TensileElongation2(Yield,3.20mm) | | ASTM638 | >5.0 | % |
| 伸长率2(断裂,3.20mm) | | ASTM638 | 35 | % |
| 弯曲模量3(3.20mm) | | ASTM790 | 2260 | MPa |
| FlexuralStrength3(3.20mm) | | ASTM790 | 72.6 | MPa |
| 冲击性能 | 悬壁梁缺口冲击强度 | 23°C,3.20mm | ASTM256 | 390 | J/m |
| 23°C,6.40mm | ASTM256 | 340 | J/m |
| 硬度 | 洛氏硬度(R级) | | ASTM785 | 100 | |
| 热性能 | 载荷下热变形温度(0.45MPa,未退火,6.40mm) | | ASTM648 | 94.0 | °C |
| DeflectionTemperatureUnderLoad(0.45MPa,Annealed,6.40mm) | | ASTM648 | 94.0 | °C |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTM648 | 87.0 | °C |
| DeflectionTemperatureUnderLoad(1.8MPa,Annealed,6.40mm) | | ASTM648 | 88.0 | °C |
| 维卡软化温度 | | ASTM15254 | 94.0 | °C |
| 可燃性 | UL阻燃等级 | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB |